SMC roving is spJMially designed as reinforcement for thermoset resin used in sheet molding compounds to product automobile parts, seats, bath tabs, water storage tanks, and sporting tools, etc. The SMC roving, treated with silane-based size, is made to achieve good compatibility with various resins. |
---------------------------------------------------------------------------------------------------------------------------------
|
PRODUCT PROPERTIES: |
TJMHNICAL REQUIREMENTS : |
|
*Easy chopped *Good strand integrity *Good dispersion *Low static *Excellent mold flow ability *Excellent mJMhanical properties |
*R2O content:<=0.80% *Coupling agent: Silane *Moisture : <=0.10% *Filament diameter : 14¦Ìm *Loss on ignition : 1.55%+_0.20% *Compatible resin : Polyester&vinylester |
PRODUCT SPJMIFICATION:
|
Product Code |
Tex value (Tex) |
Filament Diameter(¦Ìm) |
Loss on ignition (%) |
Stiffness (mm) |
|
JM13-2400C(J601-300¡Á8) |
2400 |
13-14 |
1.4¡À0.2 |
£¾130 |
|
JM13-4800C(J601-300¡Á16) |
4800 |
13-14 |
1.4¡À0.2 |
£¾130 |
|
JM13-2400C(J602-300¡Á8) |
2400 |
13-14 |
1.2¡À0.2 |
£¾130 |
|
JM13-2400C(J601-300¡Á16) |
4800 |
13-14 |
1.2¡À0.2 |
£¾130 |
|
JM13-2400C(J603-300¡Á8) |
2400 |
13-14 |
1.6¡À0.2 |
£¾130 |
|
JM13-4800C(J603-300¡Á16) |
4800 |
13-14 |
1.6¡À0.2 |
£¾130 |
SpJMial products are according to customers requirements.
INDIVIDUAL AND BULK PACKING:
*Each cheese of JM is protJMted by a plastic bag, if required, thermoplastic bag also can be used, then covered by a box with the size of 278mm¡Á278mm¡Á273mm; net weight is 16.5 to 17.5kgs.
STORAGE:
*JM roving should be stored dry and in its original packing. The best conditions are temperature between 10 and 35¡æ and at a relative between 35 and 85%.
INDIVIDUAL AND BULK PACKING:
*Each cheese of JM is protJMted by a plastic bag, if required, thermoplastic bag also can be used, then covered by a box with the size of 278mm¡Á278mm¡Á273mm; net weight is 16.5 to 17.5kgs.
STORAGE:
*JM roving should be stored dry and in its original packing. The best conditions are temperature between 10 and 35¡æ and at a relative between 35 and 85%.